تاثير معدل التبريد على خواص سبيكة Ag - Cu - Sn == Effects Of Cooling Rate On Roperties Of (Ag - Cu Sn) Ternary Alloy
Author name:
جمان حيدر ساجت
Supervisor name:
حيدر حسن جابر جمال الدين
General topic:
Production engineering metallurgy and materials
Specific topic:
Metals Engineering
Degree:
Higher Diploma
University:
University of Babylon - Faculty Of Materials Engineering - Department Of Metallurgical Engineering
Language:
English
University location:
Babylon
First pages:
46T184 - p.pdf
Abstract:
Dental fillings is widely used because of good mechanical properties and low cost but also was one of the more fillings topic of discussion and it studied continuously.The objective of this research is studing the effect of the cooling rate on the phases and properties of amalgam. two alloys were prepared by two types of casting (die casting and sand casting) with fixed percentage of tin, copper, silver and zinc for both alloys respectively about (7.5gm, 6.25gm , 10.75gm , 0.5gm).The process done by using an electric furnace in an inert gas atmosphere of argon and alloys thermally treated at a temperature (400C?) for a period of four hours for the purpose of homogenization phases alloys. And then it was studying the microstructure using an optical microscope. And using X - ray diffraction to determine the phases in alloys.The phase evaluation showed that the phases in the amalgam alloy (die alloy) has ? (Ag3Sn) , ? (Cu3Sn), and one other phase ? (Cu6Sn5) and the phases in the amalgam alloy (sand alloy) has ? (Ag3Sn) and ? (Cu3Sn). Then alloys have been converted into powder using a ball mill. The powder was treated thermally output for temperature (100C?) for a period of three hours atmosphere vacuum to remove internal stresses.The amalgam manufactured according to the ADA specification No.1 where he was mixing 0.8gm from each of the mercury and the powder for 30 seconds mined device and then put the dough, resulting in the mold of Teflon and sheds them straining compression amount (14MN / m2) for a period of 85 seconds still stress after that, the sample isextracted from the mold after the half - hour and placed in a glass chamber at a temperature of 37 ± 1C?.Microstructure of the amalgams were studied primarily by x - ray diffraction, optical microscopy.The phase analysis of two amalgams shows two phases; ?1, ?.studied the mechanical properties (tensile, compression, creep, dimensional change, hardness) and the result was that all properties effected with the change of the colling rate.It was conducted two types of corrosion tests are testing the open circuit (OCP) and potentiodynamic polarization in industrial saliva solution at a temperature of 37 ± 1C?.