دراسة بعض خصائص فيرايت الاسبنل المحضر بطريقة السيراميك والسول جيل == Studying some Properties of Spinel Ferrite preparing by Ceramic and Sol - Gel Methods
Author name:
اثير ابراهيم عبد علي الخفاجي
Supervisor name:
كاظم جواد كاظم الشجيري
General topic:
Physics
Specific topic:
Physics
Degree:
Doctorate
University:
Mustansiriyah University - College Of Science
Language:
English
University location:
Baghdad
First pages:
26T1775 - p.pdf
Abstract:
In this research three series of spinel ferrites samples where prepared which is copper - zinc ferrite with general formula (Cu1 - xZnxFe2O4), magnesium - zinc ferrite with general formula (Mg1 - xZnxFe2O4) and nickel - zinc ferrite with general formula (Ni1 - xZnxFe2O4) at (X) values ranging from 0.0 to 1.0, step of 0.2 where (X) represents the proportion of zinc in ferrite, using two preparation methods which is Conventional ceramic method and Sol - Gel method. Three sintering temperatures have been used which is (1000ºC), (1050ºC) and (1100ºC) to determine the effect of sintering temperature on the final specifications of the samples. (Network analyzer device) has been used to studding the microwaves absorption in the range of (X - band) with a frequency range (8 - 12.5 GHz). Also, X - ray diffraction analysis (XRD) has been used to determine the crystal structure and purity of the prepared samples and to calculate the average grain size and micro strain, The samples were examined using a scanning electron microscope device to evaluate the crystal size and to see distribution style after the sintering process, were Also, the density of the prepared samples were measured to calculate the porosity values.The results showed that the best samples with very high absorbency a long the (X - band) is (Mg0.6Zn0.4Fe2O4) and (Cu0.6Zn0.4Fe2O4) at sintering temperature (1100 ºC). This stability and efficiency observed firstly compared with other researches and literatures. Also the resonance peaks for all three types of spinel ferrite appeared at frequencies (8.6, 9.8, 10.0, 10.2, 11.01.11.2, 11.6, 12.0, 12.2) (GHz). X - ray diffraction results showed that all the prepared samples are a poly - crystalline also showed the occurrence of micro strain on the crystals due to effect of the sintering temperature on the crystals.Comparison between the samples prepared by Sol - Gel method and Conventional ceramic method; the result showed the homogeneity of particle size and particle distribution was the best for first method. Whereas the porosity was small for this method