تاثير اضافة مادة البايركس على بعض الخصائص الفيزيائية لمادة البورسيلن == Influence of Pyrex Addition on Some Physical Properties of Porcelain Material
Author name:
عمر عدنان جاسم
Supervisor name:
كريم علي جاسم | سوسن عبد الحسين مهدي
General topic:
Physics
Specific topic:
Solid State and Materials Physics
Degree:
Master
University:
University of Baghdad - Ibn Al-Haytham College Of Education For Pure Sciences - Physics Department
Language:
English
University location:
Baghdad
First pages:
26T1993 - p.pdf
Abstract:
This study was carried out to prepare a porcelain samples of raw material 50 wt % kaolin dukhla, 25 wt % erzma sand glass and 25 wt% feldspar, boro silicate glass (Pyrex) used as a flux in the porcelain (ceramic) body, instead of feldspar, yielding a new material which has new properties with grain size equal to 53μ.Pyrex which was added to the porcelain to get the mixtures of sample. The all mixtures prepared and 10 wt % of distilled water was added, the resulting blends were die pressed of 25 MPa, to produce specimens with diameter of 25 mm and thickness of 5 mm, then they were dried and sintered for different temperatures (1200, 1250, and 1300) C° for 1 hour in an electric furnace. Physical properties measurements such as density, porosity, water absorption and length shrinkage percentage, were carried out, also mechanical properties (compression strength) and thermal properties. (Thermal conductivity and heat capacity) were measured The result of the physical properties measurement are found to be improved at increasing the ratio of Pyrex mixture, such as increase in density and shrinkage which a company with the decrease of porosity and water absorption, also the same changes were happened for these properties with increasing sintering temperature for all mixtures, and the highest increment in shrinkage have been shown at 1250 C°.The thermal conductivity and heat capacity have increased the ratio of Pyrex mixture, and there are small increment in these measurements, at increasing temperature for mixtures 3 and 4, but the increment is high for mixture no. (2).The results of mechanical properties measurements (diametrical strength) are found to be improved and increased at the increase of the ratio of Pyrex mixture and the mixture no. (3) have a highest strength. Also this improvement and increment in strength was continued for mixtures 2 and 3, with the increase of the sintering temperature whereas decreases for mixture (4) improvement in physical and mechanical properties for a new porcelain make suit usage in brick walls industry (porcelain tiles).