تحضير وتشخيص راتنجين بوليمرين جديدين من اعادة تدوير نفايات متعدد ترفثالات الاثلين (PET) وتقييم كفاءتهما في تثبيط تاكل مادة حديد الصلب الكربوني في الوسط الحامضي 0.1 M HCl == Preparation and Characterization of TwoNew polymeric resins from recycle waste Polyethylene Terephthalate (PET) and evaluated its efficiency As to Inhibit the Corrosion of Carbon Steel alloy in Acidic Media (0.1M) HCl
Author name:
علي حسين ياسر العبادي
Supervisor name:
مؤيد نعيم خلف | علاء سامي خلف
General topic:
Chemistry
Specific topic:
Chemistry
Degree:
Master
University:
University Of Basrah - College Of Science - Chemistry Department
Language:
Arabic
University location:
Basrah
First pages:
25T1594 - p.pdf
Abstract:
The research included synthesis ,characterization and evaluation of two new corrosion inhibitors (Bis(2 - ((2 - hydroxyethyl) thio) ethyl) terephthalate (BHET) and Bis(2 - ((6 - Mono malic acid - hydroxyl ethyl ester) sulfonyl) ethyl terephthalate (BHMET) from recycled waste polyethylene terephthalate .The best percent of the two corrosion inhibitors were reached after many experiments, which included study many factors like temperature, the equivalent weight of reactants and others. The synthesized corrosion inhibitors were characterized by FTIR and 1HNMR spectroscopy and thermal analysis . As measured for inhibitors thermal stability TGA&DTA has been found to be inhibitors stable thermally It was found that the inhibitor (Bis(2 - ((2 - hydroxyethyl) thio) ethyl) terephthalate stable up to a temperature (240) ˚C and the inhibitor Bis(2 - ((6 - Mono malic acid - hydroxyl ethyl ester) sulfanyl) ethyl terephthalate stable up to a temperature (230) ˚C This is evidence of its effectiveness within these thermal grades of industrial processes, particularly their work inhibitors corrosion.The two inhibitors were evaluated as corrosion inhibitors using hydrochloric acid as corrosion media for carbon steel alloy( carbon steel C1010) . The factors effect on the rate of corrosion like temperature , concentration of inhibitor were studied by the electrochemical technique using the Tafel plot.The obtained results at temperatures range ( 298 - 328) K and concentrations (10 - 50) ppm were used to calculate many factors that determined the efficiency of the inhibitor like : corrosion rate , corrosion current , charge transfer resistance , Anodic Tafel constant , Cathodic Tafel constant , corrosion potential and inhibitor efficiency. It was observed that the corrosion rate increases with increase of temperature and decreases with increase of the inhibitor concentration in the same temperature. The Results showed that both inhibitors had very high inhibition in reducing the corrosion rate .The inhibition efficiency reached (97.1%) for (Bis(2 - ((2 - hydroxyethyl) thio) ethyl) terephthalate for the 40 ppm at (308) k and (96.2%) for the Bis(2 - ((6 - Mono malic acid - hydroxyl ethyl ester) sulfonyl) ethyl terephthalate for the 50 ppm at (298) k.Many thermodynamics functions was calculated ,activation energy Ea , activation entropy ΔS* , activation enthalpy ΔH* and free energy ΔGads during the different experiment conditions, which was indicated of the corrosion inhibition efficiency and the type of the inhibition. The obtained results showed that the two inhibitors were very efficient to reduce the corrosion rate in the acidic media and from the ΔGads data the type of adsorption was physisorption and chemisorption. because the value of ΔGads was higher than ( - 20 KJ/mol) and less than ( - 40 KJ/mol).