تحضير بعض بوليمرات قواعد شف ودراسة التشويب والتوصيلية الكهربائية لها == Synthesis And Characterization of Some Poly Schiff Base And Study Their Doping And Electrical Conductivity
Author name:
عمار فراس ابراهيم الدليمي
Supervisor name:
عماد طه بكر التكريتي | علي طه علي السامرائي
General topic:
Chemistry
Specific topic:
Chemistry
Degree:
Master
University:
Tikrit University - College Of Science - Chemistry Department
Language:
Arabic
University location:
Salahaddin
First pages:
25T1512 - p.pdf
Abstract:
يتناول البحث تحضير المونومير ثنائي الامين (M1) الناتج من تفاعل 4 - امينو اسيتو فينون مع التيرفثالدهايد بطريقة تحضير الجالكونات وكذلك تحضير سبع بوليمرات من نوع بولي قواعد شف اذ استعمل ثنائي الامين (M1) في تحضير البوليمر (I) من خلال عملية تكاثف مع التيرفثال | This research handles preparation of seven polymers of poly Schiff bases , and The di amin (M1) has been prepared from reaction of 4 - amino acetophenone with terphthaldehyde by Chalcons preparing method , where terphthaldehyde was used to prepare ( VI , V , VII ) polymers through condensation with di amines { 2,6 - di amino pyridine , 4 - amino phenyl sulfone , di amino malono nitrile } , also phtaldehyde was used to prepare ( VII , IV ) polymers by condensation with di amines ( 2,6 - diamino pyridine , 4 - amino phenyl sulfone ) , and isophthaldehyde was used in preparation of polymer (III) by condensation with { 2,6 - di amino pyridine } and below is the structure of the prepared di amine (M1). All polymers have been characterized by FT - IR technique , and some of them were characterized by CHN and 1H - NMR , Pellets preparing of all polymers where prepared with thickness range (0.97 - 0.75) with range pressure (1000 - 2000) Kg\cm2 , and then a Volume Electric doped Conductivity has been measured for the samples in their pure and doped state by using different dopants (Iodine , Ferric chloride , Zinc chloride , and p - toluene sulphonic acid) , with different mole percentage , and also The Iodine doping was carried out by vaporization tecnique , electrical conductivity of polymers have been found in pure state (fist polymer to seven polymer) as follows : ( 1.19 - 11 , 1.22E - 11 , 2,76E - 11 , 3.00E - 11 , 2.28 E - 11, 2.33E - 10 , 8.00E - 11 ) the highest value for conductivity was for polymer ( VI ) which reached 2.33E - 10 , while the highest conductivity for the doped polymers was by using dopant iodine and reach to 9.66E - 6. the effect of changing the substitution benzene and the effect of dopants on increasing conductivity of polymers where the most effective factors for increasing the conductivity.