معالجة التربة الملوثة بالنفط الخام واستخدامه في انتاج مادة طلاء تقاوم التاكل من المواد الكيميائية == Treatment of Soil Contaminated with Crude Oil and Using it in Producing Corrosion Resisting Chemicals Coating
Author name:
مؤيد عبد الله محمد
Supervisor name:
عباس فاضل عيسى | محمد علي جابر
General topic:
Physics
Specific topic:
Physics
Degree:
Master
University:
Wasit University - College Of Science - Physics Department
Language:
English
University location:
Wasit
First pages:
26T1949 - p.pdf
Abstract:
تضمن البحث ثلاث محاور : - الاول تحضير خليط بوليمري مكون من (ايبوكسي - اسفلت) وبنسب (30% - 70%), (40% - 60%), (50% - 50%), (60% - 40%), (70% - 30%) واعتمد منها النسبه الافضل (50% - 50%) كاساس في الخليط البوليمري. في المحور الثاني تحضير خليط بوليمري مكون من (اسفلت - بولي ستايرين - ايبوكسي) وحسب النسب التاليه (50% - 0% - 50%), (50% - 10% - 40%), (50% - 20% - 30%), (50% - 30% - 20%), (50% - 40% - 10%), واعتمدت افضل نسبه مقاومه للحوامض الكيمياويه (50% - 20% - 30%) تتوازن فيها الخواص الميكانيكيه. اما المحور الثالث تحضير خليط بوليمري مكون من الايبوكسي والبولي اثيلين عالي الكثافه وبنسب ايبوكسي (5% - 10% - 15% - 20% - 25%)افضل نسبه هي 15% واعطت اعلى قوة شد موازيه للسطح مقدارها 14.4 ميكاباسكال. تم دراسة العديد من الخصائص الميكانيكيه من شد موازي للسطح وشد عمودي على السطح ومقاومة انحناء, حيث اضهرت النتائج ان النماذج المحضره من الخليط البوليمري (ايبوكسي - اسفلت) يمتلك افضل الخصائص الميكانيكيه في الضروف الاعتياديه مقارنه مع النماذج الاخرى كشد موازي للسطح (1.19 - 3.24 - 16.1 - 22.2 - 27.2) ميكاباسكال, وشد عمودي على السطح (1.76 - 2.84 - 4.25 - 6.75 - 8.87) ميكاباسكال, ومقاومة انحناء (26.8 - 3.94 - 7.47 - 8.5 - 11.5)ميكاباسكال. اظهرت النتائج ايضا ان النماذج المحضره من الخليط البوليمري (اسفلت - بولي ستايرين - ايبوكسي) يتمتع بمقاومه عاليه للحوامض الكيمياويه لكنها بينت في نفس الوقت ضعف في الخواص الميكانيكيه لذلك يجب ان تكون اضافة مادة البولي ستايرين بنسب محدده مساويه الى (10% - 20% - 30% - 40%).بالاضافه الى ذلك اظهرت النتائج ان هناك انخفاض بالخواص الميكانيكيه للنماذج المحضره من الخليط البوليمري (ايبوكسي - بولي اثيلين عالي الكثافه) كلمزاادت نسبة الايبوكسي وكانت قوة الشد الموازيه للسطح (9.9 - 11.1 - 12.5 - 14.4 - 11.7 - 10.9) ميكاباسكال وقوة الشد العموديه على السطح 17.5 - 15 - 13.5 - 9.5 - 6.69 - 3.35), اما مقاومة الانحناء تكون كبيره جدا تتجاوز الحد المطلوب. | The research consists of three routes : The first route is the preparation of polymer blend which contains (epoxy - asphalt) with proportions (30% - 70%), (40% - 60%), (50% - 50%), (60% - 40%), (70% - 30%), and depends on the best that is (50% - 50%) as a principal in polymer blend in the next dimension. The second route is the preparation of polymer blend contain (asphalt - polystyrene - epoxy) with proportions about (50% - 0% - 50%), (50% - 10% - 40%), (50% - 20% - 30%), (50% - 30% - 20%), (50% - 40% - 10%), and depends on the best resistant proportion to the chemical acids (50% - 20% - 30%) in which the mechanical properties are balanced. The third one is the preparation of polymer blend contains epoxy and high density polyethylene with proportions of epoxy as (5% - 10% - 15% - 20% - 25% ), the best is (15%) as a high parallel tensile strength of the surface 14.4 MPa. Most of the mechanical properties have been studied of the parallel tensile strength of the surface and the perpendicular tensile strength on the surface and bending resistance. The results showed that the prepared samples from the polymer blend (epoxy - asphalt) has the best mechanical properties in the familiar conditions compared as with the other samples as parallel tensile of the surface (1.19 - 3.24 - 16.1 - 22.2 - 27.2) MPa and a perpendicular tensile on the surface (1.76 - 2.84 - 4.25 - 6.75 - 8.87) MPa and bending resistance (26.8 - 3.49 - 7.47 - 8.5 - 11.5)MPa. The results also showed that the prepared samples from the polymer blend (asphalt - polystyrene - epoxy) which has a high resistance of the chemical acids but at the same time they showed a weakness in the mechanical properties. So, the addition of polystyrene material in specific proportion (10% - 20% - 30% - 40%). Moreover, the results showed that there was a decrease in the mechanical properties of the prepared samples of the polymer blend (epoxy - high density polyethylene), the proportion of epoxy increased, the parallel tensile strength of the surface (9.9 - 11.1 - 12.5 - 14.4 - 11.7 - 10.9)MPa and the perpendicular tensile strength on the surface (17.5 - 15 - 13.5 - 9.5 - 6.69 - 3.35) MPa, while the bending resistance largely exceeds the required limit.